Título : ANÁLISE DA INFLUÊNCIA DO PRÉ-AQUECIMENTO NO AÇO FERRAMENTA VC131 PARA APLICAÇÃO DE REVESTIMENTO COM O AÇO ER308L ATRAVÉS DO PROCESSO DE FABRICAÇÃO GMAW
Otros títulos : RAFAEL EDWARD DE SOUZA LAGES
metadata.dc.creator: Lages, Rafael Edward de Souza
metadata.dc.contributor.advisor1: Oliveira, Fabiano Farias de
metadata.dc.description.resumo: Este trabalho aborda a utilização de solda de revestimento aplicado em aço com alto teor de carbono e ligas. Tal abordagem se justifica pela necessidade de peças cujo suas superfícies demandam de características superiores ao restante do componente, de modo a resistir ao ambiente de trabalho designado. O objetivo deste trabalho é analisar a influência do pré-aquecimento no aço ferramenta VC131 para aplicação de revestimento através do processo GMAW. Esta tarefa será realizada através deposição de camadas de revestimento do aço ER306L sobre o aço ferramenta VC131 através do processo de soldagem GMAW, onde se variou os valores de tensão e pré-aquecimento e foi realizado a comparação das amostras obtidas. A análise demonstrou pouca variação nas amostras onde não foi realizado o pré-aquecimento, o que leva a conclusão de que o pré- aquecimento é imprescindível para a soldagem do aço VC131. Outro ponto foi que a configuração onde se utilizou a menor faixa de tensão, tiveram menores percentuais de diluição, o que as torna ideais para a aplicação de revestimento já que se busca grandes larguras do cordão, altos reforços, baixas penetrações e baixos percentuais de diluição. Diferente das aplicações convencionais, onde o ideal é alta penetração para garantir a resistência da junta soldada.
Resumen : This work discusses the use of weld coating applied to high carbon steel and alloys. This approach justifies the need for parts whose surface requires more resources than the rest of the component to resist the designated work environment. The objective of this work is to analyze the influence of preheating on tool steel VC131 for coating application through the GMAW process. This task will be performed by compositing the ER306L steel cladding layers on the VC131 tool steel, through the GMAW welding process, where various stress and preheat values were performed in the comparison of uses. An analysis has shown little variation in quantities where it was not performed or preheated, or leads to the conclusion that preheating is essential for VC131 steel welding. Another point was the configuration where the lowest voltage range, the lowest dilution percentages or those ideal for coating application already in search of large cable widths, high reform, low penetration and low dilution percentages were used. Unlike conventional applications where high penetration is ideal to ensure weld joint strength.
Palabras clave : Aço ER306L
Aço Ferramenta VC 131
Revestimento por soldagem MIG
Pré-aquecimento
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
metadata.dc.language: por
metadata.dc.publisher.country: Brasil
Editorial : Fundação de Ensino e Pesquisa do Sul de Minas
metadata.dc.publisher.initials: FEPESMIG
metadata.dc.publisher.department: Centro Universitário
metadata.dc.rights: Acesso Aberto
URI : http://repositorio.unis.edu.br/handle/prefix/1229
Fecha de publicación : 12-dic-2019
Aparece en las colecciones: Engenharia Mecânica

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
Rafael Edward de Souza Lages.pdf897,27 kBAdobe PDFVisualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.