dc.description.abstractThe damask steel alloy is composed by the union of two or more types of steels that have different characteristics, which are joined by the brazing welding process. The damask steel bar used in the manufacture of blades is composed of several layers, obtained by folding and joined again by the brazing process, in an ideal pattern, between 50 and 600 layers. Damascus steel, in addition to its great beauty, also has great flexibility and hardness due to the intercalation of high-carbon and low-carbon steels. However, in this work, it will be described the process of making damask steel, the description of the tests and finally the results obtained and compare this alloy with the base steels used for its manufacture.pt_BR
dc.description.resumoA liga de aço damasco é composta pela união de dois ou mais tipos de aços que possuem características distintas, que são unidos pelo processo de soldagem por caldeamento. A barra de aço damasco utilizada na confecção de laminas é composto por varias camadas, obtidas por dobramento e unidas novamente pelo processo de caldeamento, em um padrão ideal, ficando entre 50 a 600 camadas. O aço damasco, além de grande beleza, possui também grande flexibilidade e dureza devido a intercalação de aços de alto teor de carbono e de baixo teor de carbono. Contudo, nesse trabalho, será descrito o processo de confecção do aço damasco, as descrição dos ensaios e por fim os resultados obtidos e comparar esta liga com os aços base, utilizados para a sua fabricação.pt_BR
dc.description.provenanceSubmitted by Regiane Paulino (regiane.paulino@unis.edu.br) on 2021-05-18T18:07:05Z No. of bitstreams: 1 Flávio Augusto Maciel Neuenschwander Penha 149615.pdf: 3193986 bytes, checksum: ace454b411f2e4cdef833439c7f2c984 (MD5)en
dc.description.provenanceMade available in DSpace on 2021-05-18T18:07:05Z (GMT). No. of bitstreams: 1 Flávio Augusto Maciel Neuenschwander Penha 149615.pdf: 3193986 bytes, checksum: ace454b411f2e4cdef833439c7f2c984 (MD5) Previous issue date: 2014-11-26en
dc.languageporpt_BR
dc.publisherFundação de Ensino e Pesquisa do Sul de Minaspt_BR
dc.publisher.countryBrasilpt_BR
dc.publisher.departmentCentro Universitáriopt_BR
dc.publisher.initialsFEPESMIGpt_BR
dc.rightsAcesso Abertopt_BR
dc.subjectCaldeamentopt_BR
dc.subjectAço damascopt_BR
dc.subjectCutelariapt_BR
dc.subject.cnpqCNPQ::ENGENHARIAS::ENGENHARIA MECANICApt_BR
dc.titlePROPRIEDADES MECÂNICAS DA LIGA DE AÇO DAMASCO SAE 5160 E UHB 15N20 APLICADOS A CUTELARIApt_BR
dc.title.alternativeFLAVIO AUGUSTO MACIEL NEUENSCHWANDER PENHApt_BR
dc.typeTrabalho de Conclusão de Cursopt_BR
Aparece nas coleções:Engenharia Mecânica

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
Flávio Augusto Maciel Neuenschwander Penha 149615.pdf3,12 MBAdobe PDFVisualizar/Abrir
Mostrar registro simples do item Recomendar este item Visualizar estatísticas


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.